LNP™ THERMOCOMP™ KFZ24XXP
LNP™ THERMOCOMP™ KFZ24XXP
POM(聚甲醛)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP KFZ24XXP is a compound based on Acetal Copolymer resin containing 20% Glass Fiber, 10% Milled Glass. Added features of this material include: Low Warpage, Chemically Coupled, Internally Lubricated.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 低翘曲共聚物填充增强 |
| 添加助剂 | 润滑剂 |
| 增强填充 | 20% 玻纤10% 研磨玻纤粉30% 玻纤+玻璃粉末 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.64 g/cm³
| ISO 1183 | |
密度 | 1.64 g/cm³
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.66 % | ISO 294 | flow, 24 hrs |
纵向(Flow) |
0.7 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
1.3 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) |
1.3 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.1 %
| ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
109 Mpa | ISO 527 | |
断裂(brk) |
105 Mpa | ASTM D638 | |
拉伸延伸率 | | | |
断裂(brk) |
2.5 % | ASTM D638 | |
断裂(brk) |
2.6 % | ISO 527 | |
弯曲强度 | | | |
- |
165 Mpa | ASTM D790 | |
- |
171 Mpa | ISO 178 | |
弯曲模量 | 7580 Mpa
| ASTM D790 | |
弯曲模量 | 9400 Mpa
| ISO 178 | |
拉伸模量 | 8540 Mpa
| ASTM D638 | 50 mm/min |
拉伸模量 | 8900 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
64 J/m | ASTM D256 | |
23℃ (73℉) |
6 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
534 J/m | ASTM D4812 | |
23℃ (73℉) |
36 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)峰值 |
10 J | ASTM D3763 | |
多轴冲击 | 2 J
| ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
163 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
161 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
160 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |