POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
General purpose, improved flow, minimize noise (squeak) when wearing against itself.
Celcon® M140-L1 is a general purpose acetal copolymer material with a slightly lower viscosity for improved flow in molding that has been modified to reduce or eliminate noise (squeak) when wearing against itself.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高流动共聚物降噪音 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.4 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 12 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.9 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.7 % | ISO 294-4, 2577 | |
熔体密度 | 1.17 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 63 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 9.5 % | ISO 527-2/1A | 50mm/min |
弯曲强度 | |||
3.5%应变 | 71 Mpa | ISO 178 | |
弯曲模量 | 2500 Mpa | ISO 178 | 23°C |
拉伸模量 | 2600 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5.7 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 100 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 161 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 100 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 120 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |