LNP™ LUBRICOMP™ KP004AH
POM(聚甲醛)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP KP004AH is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨均聚物 | |||
| 增强填充 | 20% PTFE+硅PTFE硅 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.49 g/cm³ | ISO 1183 | |
密度 | 1.49 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 2.14 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 2.1 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 2.1 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 2.05 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.2 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 45 Mpa | ISO 527 | |
断裂(brk) | 50 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 12.5 % | ASTM D638 | |
断裂(brk) | 10.5 % | ISO 527 | |
弯曲强度 | |||
- | 75 Mpa | ASTM D790 | |
- | 77 Mpa | ISO 178 | |
弯曲模量 | 2410 Mpa | ASTM D790 | |
弯曲模量 | 2800 Mpa | ISO 178 | |
拉伸模量 | 2200 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2400 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.25 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.16 - | ASTM D 3702 | Static COF |
磨损因数 | 9 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 48 J/m | ASTM D256 | |
23℃ (73℉) | 4 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 427 J/m | ASTM D4812 | |
23℃ (73℉) | 29 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 5 J | ASTM D3763 | |
多轴冲击 | 1 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 163 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 99 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 99 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |