Ultraform® N 2640 Z6 UNC
POM(聚甲醛)
巴斯夫 (BASF)
产品描述
Ultraform N 2640 Z6 UNC is an elastomer-modified injection molding POM grade with excellent impact strength.
Applications
Typical applications include toys components such as bicycle frames, automotive parts such as cladding elements and windshield wiper units, and clips, snap and fastening elements, and other components subject to impact stress.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.33 g/cm³ | ISO 1183 | |
比重 | 1.33 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 4.5 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.6 % | ISO 294-4 | |
横向(Across Flow) | 1.6 % | ISO 294-4 | |
- | 1.9 % | Internal | |
吸水率 | 0.25 % | ASTM D570 | 50% RH |
吸水率 | 1.1 % | ASTM D570 | Saturation |
吸水率 | 0.25 % | ISO 62 | 50% RH |
吸水率 | 1.1 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 37 Mpa | ASTM D638 | 23℃ |
屈服(yld) | 37 Mpa | ISO 527 | 23℃ |
拉伸延伸率 | |||
屈服(yld) | 17 % | ASTM D638 | 23℃ |
屈服(yld) | 17 % | ISO 527 | 23℃ |
标称断裂伸长率 | 50 % | ISO 527 | 23℃ |
弯曲模量 | 1320 Mpa | ASTM D790 | 23℃ |
拉伸模量 | 1300 Mpa | ISO 527 | 23℃ |
拉伸蠕变模量 | |||
1h | 825 Mpa | ISO 899 | |
1000h | 575 Mpa | ISO 899 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 179 | |
23℃ (73℉) | 18 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179 | |
23℃ (73℉) | NB kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 59 J/m | ASTM D256 | |
23℃ (73℉) | 155 J/m | ASTM D256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 129 °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | 130 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 71 °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ISO 75 | |
相对温度指数(RTI) | |||
冲击w/impact,1.5/1.6 mm | 50 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 50 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 50 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 50 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 50 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 50 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 130 E-6/°C | Internal | |
- | 80 E-6/°C | ASTM D E831 | |
熔融温度(Tm) | 166 °C | ASTM D3418 | |
熔融温度(Tm) | 166 °C | ISO 3146 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+11 Ohm-cm | ASTM D257 | 1.5 mm |
体积电阻率 | 1.0E+11 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+12 Ohm | ASTM D257 | 1.5 mm |
表面电阻率 | 1.0E+12 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 4.5 - | IEC 60250 | |
1MHz | 4.3 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 100 E-4 | IEC 60250 | |
1MHz | 250 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | |
绝缘强度 | 36 kV/mm | IEC 60243-1 |