Hostaform® MT® SlideX® 2404
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Tribological modified
Hostaform® MT® SlideX® 2404 is a low melt viscosity injection molding grade for fast cycling and thin walled parts with tribological modification designed for use in demanding applications that require prevention of audible noise caused by stick-slip phenomenon and low friction and wear against plastics and metals.
Hostaform® MT® SlideX® 2404 is a special grade developed for medical industry applications and complies with:
CFR 21 (177.2470) of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 11559) and the Device Master File (MAF 1079)
the corresponding EU and national registry regulatory requirements
biocompatibility in tests corresponding to USP <88> Class VI/ISO 10993
low residual monomers
no animal-derived constituents
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨低摩擦短周期成型医疗级生物相容低粘度 | |||
| 法规认证 | DMF(药品主控文件)FDA(食品药品监督管理局)ISO10993(生物相容性)MAF(设备主控文件)USP 88(美国药典生物实验)USP Class VI(美国药典) | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.4 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 25 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.9 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.8 % | ISO 294-4, 2577 | |
吸水率 | 0.6 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 50 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 2300 Mpa | ISO 178 | 23°C |
拉伸模量 | 2550 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 5.5 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 5.5 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 150 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 160 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 130 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 90 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 144 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 140 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 140 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |