Hostaform® LX90
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
general purpose unfilled molded in metallic appearance
Preliminary Data Sheet Hostaform® LX90 specialty metallic appearance grades are an integrally colored nominal 9 melt flow rate based acetal copolymer material formulated to provide an exceptional molded in metallic appearance. This product is available in many metallic molded-in-colors. Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 抗紫外线共聚物 | |||
| 添加助剂 | 紫外线稳定剂脱模剂 | |||
| 颜色形状 | 粒状金属色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.43 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 8 cm³/10min | ISO 1133 | |
吸水率 | 0.75 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 56 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 10 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 2700 Mpa | ISO 178 | 23°C |
拉伸模量 | 2700 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 5 kJ/m² | ISO 179/1eA | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 88 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |