Ultraform® S 2320 003 PRO
Ultraform® S 2320 003 PRO
POM(聚甲醛)
巴斯夫 (BASF)
产品描述
Ultraform S 2320 003 PRO is an unfilled injection molding POM grade, which supports customers in product development for the medical technology market. This grade complied with US Pharmacopoeia: Biological Reactivity Tests, USP Plastic Class VI (USP VI), ISO 10993-5: Biological Evaluation of Medical Devices Part 5: Test for Cytotoxicity, DMF: A Drug Master File (DMF) has been registered at FDA for Ultraform® PRO and Food Contact: Ultraform® PRO is in compliance with multiple regional food contact regulations, especially for Europe and United States.
Applications
This material can be used for functional parts in devices such as insulin pens or powder inhalers as well as for plug in connectors or medical device handles.
基本信息
| 原厂资料 | 物性表-ISO(英文) |
| 产品特性 | 食品接触级医疗级共聚物 |
| 法规认证 | DMF(药品主控文件)EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局)ISO10993(生物相容性)REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质)USP Class VI(美国药典) |
| 成型方式 | 注塑 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.4 g/cm³
| ISO 1183 | |
熔体体积流动速率(MVR) | | | |
190℃/2.16 kg |
11 cm³/10min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
2.1 % | ISO 294-4 | |
横向(Across Flow) |
2.1 % | ISO 294-4 | |
吸水率 | 0.2 %
| ISO 62 | equilibrium 23°C/50% r.h. |
吸水率 | 0.8 %
| ISO 62 | equilibrium in water at 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
65 Mpa | ISO 527-1/-2 | 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
9 % | ISO 527-1/-2 | 50 mm/min |
标称断裂伸长率 |
28 % | ISO 527-1/-2 | 50 mm/min |
拉伸模量 | 2700 Mpa
| ISO 527-1/-2 | |
拉伸蠕变模量 | | | |
1000h |
1300 Mpa | ISO 899-1 | strain <= 0,5%, 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
5 kJ/m² | ISO 179/1eA | |
23℃ (73℉) |
5.5 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
170 kJ/m² | ISO 179/1eU | |
23℃ (73℉) |
180 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 145 Mpa
| ISO 2039-1 | at 358 N and 30 s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
100 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
110 E-6/K | ISO 11359-1/-2 | 23-55℃ |
熔融温度(Tm) | 167 °C
| ISO 11357-1/-3 | DSC |
短周期使用温度 | 100 °C
| - | |
加工温度 | 190~230 °C
| - | injection |
模具温度 | 60~120 °C
| - | injection |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
1.6 mm | IEC 60695-11-10 | |
FMVSS | + pass
| FMVSS 302 | thickness d>= 1mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m
| IEC 60093 | |
表面电阻率 | 1.0E+13 Ohm
| IEC 60093 | |
介电常数(DK) | | | |
1MHz |
3.8 - | IEC 60250 | |
耗散因数(DF) | | | |
1MHz |
50 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | | | |
溶液A |
600 V | IEC 60112 | |