LNP™ LUBRICOMP™ KI001XXJ
POM(聚甲醛)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP KI001XXJ is a compound based on Acetal containing 2% Silicone. Added features of this grade include: Wear Resistant, Healthcare.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨医疗级 | |||
| 增强填充 | 2% 硅 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.4 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 2.4 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 2.4 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.24 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 52 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 16 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 46 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
屈服(yld) | 74 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2280 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2750 Mpa | ASTM D638 | 50 mm/min |
摩擦系数 | 0.44 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.34 - | ASTM D 3702 | Static COF |
磨损因数 | 22 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 81 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1550 J/m | ASTM D4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 106 °C | ASTM D648 | 3.2 mm, unannealed |