LubriOne™ 5209 FPL 20 Natural
POM(聚甲醛)
埃万特(原普立万)(Avient)
产品描述
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨低摩擦共聚物 | |||
| 添加助剂 | 润滑剂 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 颜色形状 | 粒状本色 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.51 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 8 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 2~3 % | ASTM D 955 | |
横向(Across Flow) | 1~3 % | ASTM D 955 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 45 Mpa | ASTM D638 | Type I, 5.1 mm/min |
拉伸延伸率 | |||
断裂(brk) | 26 % | ASTM D638 | Type I, 5.1 mm/min |
弯曲强度 | |||
- | 68.3 Mpa | ASTM D790 | 1.3 mm/min |
弯曲模量 | 1790 Mpa | ASTM D790 | 1.3 mm/min |
拉伸模量 | 2420 Mpa | ASTM D638 | Type I, 5.1 mm/min |
摩擦系数 | 0.12 - | ASTM 1894 | vs. Steel - Dynamic |
摩擦系数 | 0.13 - | ASTM 1894 | vs. Steel - Static |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 37 J/m | ASTM D256 | 3.18 mm, Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 153 °C | ASTM D648 | Unannealed, 6.35 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 87.8 °C | ASTM D648 | Unannealed, 6.35 mm |