LubriOne™ ATH-XC-361E
POM(聚甲醛)
埃万特(原普立万)(Avient)
产品描述
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨低摩擦均聚物 | |||
| 添加助剂 | 润滑剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.5 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 2~2.3 % | ASTM D 955 | |
吸水率 | 0.02 % | ASTM D570 | 24 hr, 3.18 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 50.3 Mpa | ASTM D638 | Type I, 5.1 mm/min |
拉伸延伸率 | |||
断裂(brk) | 10~12 % | ASTM D638 | Type I, 5.1 mm/min |
弯曲强度 | |||
- | 81.4 Mpa | ASTM D790 | |
弯曲模量 | 2340 Mpa | ASTM D790 | |
拉伸模量 | 2410 Mpa | ASTM D638 | Type I, 5.1 mm/min |
摩擦系数 | 0.25 - | ASTM 1894 | vs. Steel - Dynamic |
摩擦系数 | 0.14 - | ASTM 1894 | vs. Steel - Static |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 48 J/m | ASTM D256 | 3.18 mm, Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 124 °C | ASTM D648 | Unannealed, 6.35 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 116 °C | ASTM D648 | Unannealed, 6.35 mm |