LNP™ THERMOCOMP™ KF002XXP
LNP™ THERMOCOMP™ KF002XXP
POM(聚甲醛)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP KF002XXP is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. Added features of this material include: Chemically Coupled.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 填充增强 |
| 增强填充 | 10% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.45 g/cm³
| ISO 1183 | |
密度 | 1.45 g/cm³
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
1.16 % | ISO 294 | flow, 24 hrs |
纵向(Flow) |
1.2 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
1.3 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) |
1.29 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.35 %
| ISO 62 | 23°C / 50% RH |
吸湿率 | 0.1 %
| ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
86 Mpa | ISO 527 | |
断裂(brk) |
84 Mpa | ASTM D638 | |
拉伸延伸率 | | | |
断裂(brk) |
3.2 % | ASTM D638 | |
断裂(brk) |
3.4 % | ISO 527 | |
弯曲强度 | | | |
- |
124 Mpa | ASTM D790 | |
- |
137 Mpa | ISO 178 | |
弯曲模量 | 4610 Mpa
| ASTM D790 | |
弯曲模量 | 5400 Mpa
| ISO 178 | |
拉伸模量 | 4750 Mpa
| ASTM D638 | 50 mm/min |
拉伸模量 | 5400 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
48 J/m | ASTM D256 | |
23℃ (73℉) |
5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
448 J/m | ASTM D4812 | |
23℃ (73℉) |
33 kJ/m² | ISO 180/1U | 80*10*4 |
多轴冲击 | 1 J
| ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
164 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
161 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
161 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |