LNP™ THERMOCOMP™ KF005
POM(聚甲醛)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP* KF005 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber. Added features of this material include: Chemically Coupled.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 共聚物填充增强 | |||
| 增强填充 | 25% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.6 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.6~0.9 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1~4 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.28 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.28 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 100 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 107 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 4.2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 3.5 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
断裂(brk) | 38 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 540 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 10160 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 12920 Mpa | ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 69 J/m | ASTM D256 | |
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 701 J/m | ASTM D4812 | |
23℃ (73℉) | 38 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 163 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 164 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 162 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 161 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 7.1E+7 E-6/°C | ASTM D 696 | -30°C to 30°C, flow |
横向(Across Flow) | 7.3E+7 E-6/°C | ASTM D 696 | -30°C to 30°C, xflow |