Hostaform® MT12U03
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Improved flow grade with optimum properties and higher stiffness for medical technology applications
Hostaform® MT12U03 is a moderately high flow grade for faster cycling and thin walled injection molding with improved stiffness and hardness compared to Hostaform® MT12U01.
Hostaform® MT12U03 is a special grade developed for medical industry applications and complies with:
CFR 21 (177.2470) of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 11559) and the Device Master File (MAF 1079)
the corresponding EU and national registry regulatory requirements
biocompatibility in tests corresponding to USP<88>Class VI/ISO 10993<!--88-->
low residual monomers
no animal-derived constituents
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性短周期成型医疗级生物相容高流动共聚物 | |||
| 添加助剂 | 脱模剂 | |||
| 法规认证 | DMF(药品主控文件)FDA(食品药品监督管理局)ISO10993(生物相容性)MAF(设备主控文件)USP 88(美国药典生物实验)USP Class VI(美国药典) | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 12 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.8 % | ISO 294-4, 2577 | |
吸水率 | 0.65 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 70 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 28 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 3000 Mpa | ISO 178 | 23°C |
拉伸模量 | 3100 Mpa | ISO 527-2/1A | |
拉伸蠕变模量 | |||
1h | 2750 Mpa | ISO 899-1 | |
1000h | 1450 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 200 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 200 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5.5 kJ/m² | ISO 180/1A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 156 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 107 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 158 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 120 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 170 °C | ISO 11357-1/-3 | 10°C/min |