Plexiglas® HFI10
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Plexiglas® HFI10 is an impact modified thermoplastic acrylic resin formulated for injection molding. It has high melt flow, enhanced mold release properties and provides 10 times the impact resistance of standard acrylics while maintaining excellent optical properties. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Supplemental moldflow simulation data is available.
基本信息
| 原厂资料 | 物性表-ASTM(英文) 宣传册 (英文) | |||
| 产品特性 | 高冲击良好光学性耐刮擦易脱模抗紫外线耐候性高流动 | |||
| 添加助剂 | 抗冲击剂 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.15 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 3.3 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.3~0.8 % | ASTM D 955 | |
吸水率 | 0.4 % | ASTM D570 | 24 hr immersion |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 37.9 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 50 % | ASTM D638 | |
弯曲强度 | |||
断裂(brk) | 71 Mpa | ASTM D790 | |
弯曲模量 | 1860 Mpa | ASTM D790 | |
拉伸模量 | 1860 Mpa | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 48 J/m | ASTM D256 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 38 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 88.9 °C | ASTM D648 | annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 79.4 °C | ASTM D648 | annealed |
维卡软化温度(Vicat) | 93.9 °C | ASTM D1525 | 50°C/hr; 10N |
维卡软化温度(Vicat) | 82.8 °C | ASTM D1525 | 50°C/hr; 50N |
导热系数 | 0.22 W/(m K) | ASTM C 177 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | ASTM D 635 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 90 % | ASTM D1003 | 3.2 mm |
雾度 | 1 % | ASTM D1003 | 3.2 mm |
折射率 | 1.49 - | ASTM D542 | Nd @ 72°F |