PLEXIGLAS® Resist zk50 is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
Typical properties of impact-modified PLEXIGLAS® molding compounds are
• excellent transmission and clarity
• brilliant appearance
• the pleasant feel and sound of the moldings.
PLEXIGLAS® Resist zk50 is characterized by the following special properties:
• maximum break resistance and impact strength
• improved resistance to stress cracking
• certified dishwasher resistance
Application:
Used for injection molding. Profile extrusion or coextrusion are also possible
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性透光良好表面耐洗涤剂 | |||
| 添加助剂 | 抗冲击剂 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出共挤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.12 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 0.1 cm³/10 min | ISO 1133 | |
吸湿率 | 0.42 % | ISO 62 | 23°C / 50% |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 25 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527 | 50 mm/min |
拉伸模量 | 950 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 13 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 73 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ISO 75 | |
维卡软化温度(Vicat) | 75 °C | ISO 306/B50 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 150 E-6/K | ISO 11359 | 0-50 °C |
玻璃化温度(Tg) | 115 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | IEC 60695-11-10 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 89 % | ISO 13468-2 | 3mm, D65 |
折射率 | 1.49 - | ISO 489 | 3mm, 589nm/23°C |