CYROLITE® MD H12
PMMA(亚克力)
罗姆化学(原赢创)(Rohm/Roehm Chemical)
产品描述
CYROLITE® MD H12 acrylic polymer is an amorphous thermoplastic molding compound based on polymethyl methacrylate (PMMA) for the medical diagnostic industry.
Typical properties of CYROLITE® MD acrylic polymers are:
• Exceptional ultra-violet light transmittance
• Superior optical clarity
• Maximum flow characteristics
• Excellent dimensional stability
• Outstanding scratch resistance
• Total cost-of-use advantage over glass
The special properties of CYROLITE® MD H12 polymer are:
• Higher Vicat softening point
• Medium melt flow rate
Application:
Used for injection molding of medical devices requiring UV spectroscopy for fluid evaluation.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热良好光学性透光耐刮擦尺寸稳定食品接触级医疗级抗紫外线中粘度 | |||
| 法规认证 | FDA(食品药品监督管理局)ISO10993(生物相容性)USP Class VI(美国药典) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 7 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.4~0.6 % | ASTM D 955 | |
吸水率 | 0.3 % | ASTM D570 | |
堆积(视)密度 | 0.66 g/cm³ | ASTM D 1895 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 65.5 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
屈服(yld) | 4~6 % | ASTM D638 | |
断裂(brk) | 4~6 % | ASTM D638 | |
弯曲强度 | |||
- | 117.2 Mpa | ASTM D790 | |
弯曲模量 | 3400 Mpa | ASTM D790 | |
拉伸模量 | 3200 Mpa | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 19 J/m | ASTM D256 | 6.35 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 94 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 95 °C | ASTM D648 | Annealed, 6.35 mm |
维卡软化温度(Vicat) | 105 °C | ASTM D1525 | |
线性膨胀系数(CLTE) | |||
- | 72 E-6 mm/mm/℃ | ASTM D 696 | 0 to 100°C |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | 3.20 mm |
透光率 | 87.7 % | ASTM D1003 | 3.20 mm, 340 nm UV |
雾度 | 1 % | ASTM D1003 | 3.20 mm |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
黄色指数(YI) | 1 - | ASTM D 1925 | 3.20 mm |