ACRYLITE® Resist AG 100
PMMA(亚克力)
赢创(原德固赛)(Evonik)
产品描述
ACRYLITE® Resist AG 100 is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).
Properties
ACRYLITE® molding compounds have the following typical properties:
high weather resistance
excellent transmission and clarity
brilliant appearance
low weight - half the weight of glass
100% recyclable - best life cycle assessment as compared with glass and PC
pleasant feel and sound of molded parts
ACRYLITE® Resist AG 100 is characterized by the following additional properties:
highest breaking strength and impact strength (30 times higher breaking strength than glass)
improved resistance to stress cracking
balanced property profile
clear reduction of reversible haze at very high and low temperatures
increased heat deflection temperature under load
AMECA listing, CAMPUS and moldflow data available
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热导光良好表面耐候性ESCR | |||
| 法规认证 | AMECA(美国加拿大汽车认证) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出片材挤出吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.16 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 1.1 cm³/10 min | ISO 1133 | |
260℃/3.8 kg | 7.7 cm³/10 min | ISO 1133 | |
吸水率 | 1.5 % | ISO 62 | in water |
吸湿率 | 0.5 % | ISO 62 | 23°C / 50 % |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527 | 50 mm/min |
标称断裂伸长率 | 45 % | ISO 527 | |
拉伸模量 | 2200 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 120 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 105 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 100 °C | ISO 75 | |
维卡软化温度(Vicat) | 105 °C | ISO 306 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 110 E-6/K | ISO 11359 | 0-50 °C |
玻璃化温度(Tg) | 112 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | IEC 60707 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ISO 13468-2 | 3mm, D65 |
雾度 | 0.7 % | ASTM D1003 | 3mm |
折射率 | 1.49 - | ISO 489 | 3mm |