CYROLITE® Med 2 is a PMMA-based copolymer for injection molding and extrusion of medical applications.
Typical properties of CYROLITE® acrylic-based copolymer compounds are:
• High Light Transmittance with little haze
• 5 times the impact resistance of unmodified acrylics
• Resistant to body fluids and many chemicals
• Excellent bonding to PVC tubing
• Can be thermal bonded, ultrasonic and laser welded
• Good heat resistance
• Resistance to EtO, gamma and E-beam sterilization
The special properties of CYROLITE® Med 2 are:
• Superior resistance to lipids, blood, and oncology drugs
• Excellent resistance to alcohols and disinfectant wipes
• Excellent ductility
Application:
Used for injection molding and extrusion of medical device and diagnostics industries.
基本信息
| 原厂资料 | 物性表(英文)-ISO 物性表(英文)-ASTM | |||
| 产品特性 | 高冲击耐热透光良好粘合性无双酚A(BPA)医疗级电子束灭菌耐伽马射线环氧乙烷灭菌(EtO)耐化学性耐酒精耐脂(肪) | |||
| 法规认证 | ISO10993(生物相容性)USP Class VI(美国药典) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.1 g/cm³ | ISO 1183 | |
比重 | 1.08 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 0.6 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/5 kg | 2.1 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.5~0.7 % | ASTM D 955 | |
吸水率 | 0.38 % | ASTM D570 | |
堆积(视)密度 | 0.65 g/cm³ | ASTM D 1895 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 31 Mpa | ISO 527 | 50 mm/min |
- | 36.7 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
屈服(yld) | 3.9 % | ASTM D638 | |
屈服(yld) | 3.6 % | ISO 527 | 50 mm/min |
断裂(brk) | 22 % | ASTM D638 | |
标称断裂伸长率 | 34 % | ISO 527 | |
弯曲强度 | |||
- | 59.2 Mpa | ASTM D790 | |
弯曲模量 | 1600 Mpa | ASTM D790 | |
拉伸模量 | 1700 Mpa | ASTM D638 | |
拉伸模量 | 1600 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 16.6 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 174 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 117 J/m | ASTM D256 | 6.4mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 33 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 82.5 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 73 °C | ASTM D648 | 6.4mm, Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 76.4 °C | ISO 75 | |
维卡软化温度(Vicat) | 94 °C | ASTM D1525 | 50N, 50°C/h |
维卡软化温度(Vicat) | 81 °C | ISO 306/B50 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 86 E-6/°C | ASTM D 696 | 0 - 100°C |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 85 % | ASTM D1003 | 3.2 mm |
透光率 | 85.7 % | ISO 13468-2 | 3mm, D65 |
雾度 | 7 % | ASTM D1003 | 3.2 mm |
雾度 | 7 % | ASTM D1003 | 3mm |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
黄色指数(YI) | -1 - | ASTM E 313 | 3.2 mm |