PLEXIGLAS® Hi-Gloss FT15 black 9V022
PMMA(亚克力)
罗姆化学(原赢创)(Rohm/Roehm Chemical)
产品描述
PLEXIGLAS® Hi-Gloss FT15 black 9V022 is a special acrylic-based polymer.
With regard to its
• high mar resistance
• good weather resistance
• good polishability,
PLEXIGLAS® Hi-Gloss FT15 9V022 shows comparable properties to those of PLEXIGLAS® standard molding compounds.
In addition, PLEXIGLAS® Hi-Gloss FT15 9V022 offers the special benefit of a
• high heat deflection temperature combined with good flow.
Application:
PLEXIGLAS® Hi-Gloss FT15 9V022 is particularly suitable for injection molding technical components. Owing to ist superior brilliance, high-gloss (Class A) black surfaces can be obtained in.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热高光泽镜面效果耐刮擦良好流动性 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 4.5 cm³/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 50 Mpa | ISO 527 | 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3.1 % | ISO 527 | 5 mm/min |
拉伸模量 | 3500 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 18 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 107 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 105 °C | ISO 75 | |
维卡软化温度(Vicat) | 115 °C | ISO 306/B50 | |
玻璃化温度(Tg) | 121 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
灼热丝点燃温度(GWIT) | |||
- | 675 °C | IEC 60695-2-13 |
原材料现货供应: