XT® Polymer 375
PMMA(亚克力)
赢创(原德固赛)(Evonik)
产品描述
XT polymer 375 compound is an impact-modified acrylic-based multipolymer for molding, extrusion and blow molding applications.
Typical properties of XT® polymer acrylic-based multipolymer compounds are:
outstanding thermoformability
superior heat distortion temperatures
excellent bonding and welding capabilities
good impact strength
good light transmission
resistant to EtO, gamma and E-beam sterilization
resistant to PVC stabilizers
BPS, BPA, and DEHP free
The special properties of XT polymer 375 compound are:
excellent chemical resistance
high impact strength
Application:
Used for medical devices, food packaging, pharmaceutical packaging, rigid medical device packaging and appliance parts.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 高冲击耐热热稳定良好粘合性易焊接食品接触级无双酚A(BPA)无双酚S(BPS)无DEHP (DOP)医疗级电子束灭菌环氧乙烷灭菌(EtO)耐化学性 | |||
添加助剂 | 抗冲击剂 | |||
法规认证 | FDA(食品药品监督管理局)ISO10993(生物相容性)USP Class VI(美国药典) | |||
颜色形状 | 粒状透明 | |||
成型方式 | 注塑挤出吹塑 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
比重 | 1.11 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/5 kg | 2.6 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.4~0.7 % | ASTM D 955 | |
吸水率 | 0.3 % | ASTM D570 | |
堆积(视)密度 | 0.65 g/cm³ | ASTM D 1895 | |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 48.3 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
屈服(yld) | 4 % | ASTM D638 | |
断裂(brk) | 28 % | ASTM D638 | |
弯曲强度 | |||
- | 75.8 Mpa | ASTM D790 | |
弯曲模量 | 2400 Mpa | ASTM D790 | |
拉伸模量 | 2600 Mpa | ASTM D638 | |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
0℃ (32℉) | 85 J/m | ASTM D256 | 6.35 mm |
23℃ (73℉) | 107 J/m | ASTM D256 | 6.35 mm |
硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 45 M | ASTM D 785 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)(18.6kg/cm²) | 86 °C | ASTM D648 | Annealed, 6.35 mm |
维卡软化温度(Vicat) | 103 °C | ASTM D1525 | |
线性膨胀系数(CLTE) | |||
- | 90 E-6 mm/mm/℃ | ASTM D 696 | 0 to 100°C |
光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 86 % | ASTM D1003 | 3.20 mm |
雾度 | 2.5 % | ASTM D1003 | 3.20 mm |
其他性能 | 值/单位 | 测试标准 | 测试条件 |
黄色指数(YI) | -1 - | Internal | 3.20 mm |