PLEXIGLAS® Satinice df33 zk6BR
PMMA(亚克力)
赢创(原德固赛)(Evonik)
产品描述
PLEXIGLAS® Satinice df33 zk6BR, based on PLEXIGLAS® Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light.
Typical properties of impact modified PLEXIGLAS® molding compound are
high break resistance and impact strength
improved resistance to stress cracking
good weather resistance
high surface hardness and mar resistance
the pleasant feel and sound of the moldings.
Extruded parts from PLEXIGLAS® Satinice df33 zk6BR are characterized by the following special properties:
excellent light diffusion combined with excellent light transmission
semi-gloss surfaces
touch and fingerprint resistant.
Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry, but also for injection molding items for lighting engineering applications.
Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击光扩散导光低光泽耐候性 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 挤出片材挤出型材挤出共挤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.16 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 1.4 cm³/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 45 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 4 % | ISO 527 | 50 mm/min |
标称断裂伸长率 | 25 % | ISO 527 | |
拉伸模量 | 2000 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 40 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 99 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 96 °C | ISO 75 | |
维卡软化温度(Vicat) | 99 °C | ISO 306 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 92 E-6/K | ISO 11359 | 0 - 50°C |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
灼热丝点燃温度(GWIT) | |||
- | 700 °C | IEC 60695-2-13 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 67 % | ISO 13468-2 | 3 mm, D65 |