Altuglas® V920
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Altuglas® V 920T / V 920 Injection moulding resin with high flow and heat resistance.
Altuglas® V Resins Non impact-modified resins exhibit the following features:
> Greatest optical performances of all existing thermoplastic materials (92% LT / 0.5% haze) to ensure crystal sparkle and brilliance even at high thickness,
> Outstanding resistance to mechanical damage and discoloration by ultraviolet rays; years of outdoor exposure have no visible effect on Altuglas® PMMA,
> Unsurpassed surface hardness (Rockwell M-Scale) and hence scratch resistance ensuring a lasting premium look,
> Higher heat resistance than impact-modified grades (Vicat B50 up to 108°C),
> Good stiffness,
> Delicate feel and sound,
> Ease of colouring (PMMA based MB required for non opaque colours to avoid optical defects).
Altuglas® V Resins have, over the years, demonstrated their outstanding performance and benefit and are thus widely used today in the most demanding applications such as automotive tail lights and instrument clusters, light fittings, household appliances, mobile phone displays, optical parts and cosmetic jars, etc. For both injection and extrusion, no matter how critical the part is, you will find an Altuglas® V Resin to address your processing needs through the wide MFI range (from 2 to 14.5) and custom lubrications available.
基本信息
原厂资料 | 物性表(英文) 宣传册 (英文) | |||
产品特性 | 耐热颜色稳定/易着色抗紫外线高流动 | |||
颜色形状 | 粒状透明 | |||
成型方式 | 注塑 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.18 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 8 g/10 min | ISO 1133 | |
收缩率 | |||
- | 0.2~0.6 % | ASTM D 955 | |
吸水率 | 0.3 % | ISO 62 | |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 69 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
断裂(brk) | 6 % | ISO 527-2 | |
弯曲模量 | 3300 Mpa | ISO 178 | |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 2 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
- | 11 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
- | 1.8 kJ/m² | ISO 180/1A | |
硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 95 M | ASTM D 785 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)(18.6kg/cm²) | 90 °C | ISO 75-2 | |
维卡软化温度(Vicat) | 101 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
- | 70 E-6/K | ASTM D 696 | |
燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | |
雾度 | 0.5 % | ASTM D1003 | |
折射率 | 1.49 - | ASTM D542 | Method B |