Altuglas® VSUVT
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Altuglas® VSUVT resin provides exceptional UV transmission and excellent transparency, making it an outstanding choice for in vitro diagnostics use. The UV transmission of Altuglas® VSUVT is considerably higher than all non-acrylic materials. In addition, Altuglas® VSUVT resin is generally tougher than UV transmitting styrenics, a common material used for this purpose. Altuglas® VSUVT acrylic resin provides devices with the outstanding optical properties needed for diagnostic accuracy.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击良好光学性导光颜色稳定/易着色易成型短周期成型良好粘合性易焊接医疗级生物相容电子束灭菌耐伽马射线环氧乙烷灭菌(EtO)ESCR耐化学性耐酸耐碱耐酒精耐脂(肪) | |||
| 法规认证 | ISO10993(生物相容性)USP Class VI(美国药典) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.18 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 28 g/10 min | ISO 1133 | |
收缩率 | |||
- | 0.2~0.6 % | ASTM D 955 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 66 Mpa | ISO 527 | |
拉伸延伸率 | |||
断裂(brk) | 5 % | ISO 527 | |
弯曲强度 | |||
- | 97 Mpa | ISO 178 | |
弯曲模量 | 2900 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 2 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 11 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 1.8 kJ/m² | ISO 180 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 84 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 80 °C | ISO 75 | |
维卡软化温度(Vicat) | 95 °C | ISO 306 | A50 (10 N) |
维卡软化温度(Vicat) | 93 °C | ISO 306 | B50 (50 N) |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 3 mm | UL94 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | 3mm |
雾度 | 0.5 % | ASTM D1003 | 3mm |
折射率 | 1.48 - | ISO 489 | Method A |