ACRYLITE® 8N acrylic polymer is an amorphous thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).
Typical properties of ACRYLITE® acrylic polymers are:
excellent weather resistance
high light transmission
high mechanical strength
high surface hardness and mar resistance
good melt flow rate
versatile colorability due to crystal clarity
The special properties of ACRYLITE 8N polymer are:
highest heat resistance
high melt strength
UV light absorption options
low levels of lubricant
AMECA listed
Application
Used for injection molding commercial and residential lighting lenses, automotive lenses and parts, optical devices and extruded profiles.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热导光抗紫外线耐候性高流动高熔体强度 | |||
| 添加助剂 | 润滑剂 | |||
| 法规认证 | AMECA(美国加拿大汽车认证) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出型材挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.19 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 3.3 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.4~0.7 % | ASTM D 955 | |
吸水率 | 0.3 % | ASTM D570 | |
堆积(视)密度 | 0.66 g/cm³ | ASTM D 1895 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 77.9 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
屈服(yld) | 4~6 % | ASTM D638 | |
断裂(brk) | 4~6 % | ASTM D638 | |
弯曲强度 | |||
- | 111.7 Mpa | ASTM D790 | |
弯曲模量 | 3500 Mpa | ASTM D790 | |
拉伸模量 | 3200 Mpa | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 19 J/m | ASTM D256 | 6.35 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 95 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 100 °C | ASTM D648 | Annealed, 6.35 mm |
维卡软化温度(Vicat) | 108 °C | ASTM D1525 | |
线性膨胀系数(CLTE) | |||
- | 72 E-6 mm/mm/℃ | ASTM D 696 | 0 to 100°C |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | 3.20 mm |
雾度 | 1 % | ASTM D1003 | 3.20 mm |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
黄色指数(YI) | 1 - | Internal | 3.20 mm |