Altuglas® VML

Altuglas® VML

Altuglas® VML

PMMA(亚克力)

阿科玛Altuglas (Arkema)

产品描述

Altuglas® VML lubricated version of VM intended for injection moulding of complex bulk pieces at lower temperatures while maintaining a perfect crystal look.

Altuglas® V Resins Non impact-modified resins exhibit the following features:

> Greatest optical performances of all existing thermoplastic materials (92% LT / 0.5% haze) to ensure crystal sparkle and brilliance even at high thickness,

> Outstanding resistance to mechanical damage and discoloration by ultraviolet rays; years of outdoor exposure have no visible effect on Altuglas® PMMA,

> Unsurpassed surface hardness (Rockwell M-Scale) and hence scratch resistance ensuring a lasting premium look, 

> Higher heat resistance than impact-modified grades (Vicat B50 up to 108°C),

> Good stiffness,

> Delicate feel and sound, 

> Ease of colouring (PMMA based MB required for non opaque colours to avoid optical defects).

Altuglas® V Resins have, over the years, demonstrated their outstanding performance and benefit and are thus  widely used today in the most demanding applications such as automotive tail lights and instrument clusters, light fittings, household appliances, mobile phone displays, optical parts and cosmetic jars, etc. For both injection and extrusion, no matter how critical the part is, you will find an Altuglas® V Resin to address your processing needs through the wide MFI range (from 2 to 14.5) and custom lubrications available.

基本信息
原厂资料
物性表(英文)
宣传册 (英文)
产品特性
高刚性
耐热
颜色稳定/易着色
抗紫外线
高流动
添加助剂
润滑剂
颜色形状
粒状
透明
成型方式
注塑
挤出
技术参数
物理性能 值/单位 测试标准 测试条件

密度

1.18 g/cm³ ISO 1183

熔体质量流动速率(MFR)

230°C/3.8 kg

14.5 g/10 min ISO 1133

收缩率

-

0.2~0.6 % ASTM D 955

吸水率

0.3 % ISO 62
机械性能 值/单位 测试标准 测试条件

拉伸强度

-

65 Mpa ISO 527-2

拉伸延伸率

断裂(brk)

5 % ISO 527-2

弯曲模量

3100 Mpa ISO 178
冲击性能 值/单位 测试标准 测试条件

简支梁缺口(Charpy Notched)

-

2 kJ/m² ISO 179

简支梁无缺口(Charpy Unnotched)

-

11 kJ/m² ISO 179

悬臂梁缺口(Izod Notched)

-

1.8 kJ/m² ISO 180/1A
硬度性能 值/单位 测试标准 测试条件

洛氏硬度 M

89 M ASTM D 785
热学性能 值/单位 测试标准 测试条件

热变形温度(HDT)

1.8 Mpa (264 psi)(18.6kg/cm²)

77 °C ISO 75-2

维卡软化温度(Vicat)

90 °C ISO 306/B50

线性膨胀系数(CLTE)

-

70 E-6/K ASTM D 696
燃烧性能 值/单位 测试标准 测试条件

UL 防火等级

HB

- mm UL94
光学性能 值/单位 测试标准 测试条件

透光率

92 % ASTM D1003

雾度

0.5 % ASTM D1003

折射率

1.49 - ASTM D542
Method B