Plexiglas® MI7
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Plexiglas® MI7 is an impact modified thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is heat resistant, has high melt flow and provides 7 times the impact resistance of standard acrylics while maintaining excellent optical properties. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Supplemental moldflow simulation data is available.
基本信息
| 原厂资料 | 物性表-ASTM(英文) 宣传册 (英文) 物性表-ISO(英文) | |||
| 产品特性 | 高冲击耐热热稳定颜色稳定/易着色耐刮擦尺寸稳定无双酚A(BPA)抗紫外线耐候性高流动 | |||
| 添加助剂 | 抗冲击剂 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.17 g/cm³ | ISO 1183 | |
比重 | 1.17 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 3.8 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 3.2 g/10 min | ASTM D 1238 | |
230°C/3.8 kg | 4.3 g/10 min | ISO 1133 | |
收缩率 | |||
- | 0.3~0.6 % | ASTM D 955 | |
- | 0.3~0.6 % | ISO 294 | |
吸水率 | 0.3 % | ASTM D570 | 24 hr immersion |
吸水率 | 0.3 % | ISO 62 | Method 1, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ISO 527-2/1A/5 | |
断裂(brk) | 48.3 Mpa | ASTM D638 | |
断裂(brk) | 45 Mpa | ISO 527-2/1A/5 | |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527-2/1A/5 | |
断裂(brk) | 35 % | ASTM D638 | |
断裂(brk) | 35 % | ISO 527-2/1A/5 | |
弯曲强度 | |||
断裂(brk) | 77.2 Mpa | ASTM D790 | |
- | 70 Mpa | ISO 178/A | Conventional Deflection |
弯曲模量 | 2380 Mpa | ASTM D790 | |
弯曲模量 | 2400 Mpa | ISO 178/A | |
拉伸模量 | 2520 Mpa | ASTM D638 | |
拉伸模量 | 2500 Mpa | ISO 527-2/1A/1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 3 kJ/m² | ISO 179-1/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
- | 40 kJ/m² | ISO 179-1/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 32 J/m | ASTM D256 | |
- | 5 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 68 M | ISO 2039-2 | |
洛氏硬度 M | 68 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 91.1 °C | ASTM D648 | annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 88 °C | ISO 75-2/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 85 °C | ASTM D648 | annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 83 °C | ISO 75-2/A | |
维卡软化温度(Vicat) | 88 °C | ASTM D1525 | 50°C/hr; 10N |
维卡软化温度(Vicat) | 83 °C | ASTM D1525 | 50°C/hr; 50N |
维卡软化温度(Vicat) | 92 °C | ISO 306/B50 | 50N |
维卡软化温度(Vicat) | 99 °C | ISO 306/A50 | 10N |
导热系数 | 0.2 W/(m K) | ASTM C 177 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ASTM D1003 | 0.125 in/3.2 mm |
透光率 | 91 % | ASTM D1003 | 3.2 mm |
雾度 | 2 % | ASTM D1003 | 0.125 in/3.2 mm |
雾度 | 2 % | ASTM D1003 | 3.2 mm |
折射率 | 1.49 - | ASTM D542 | Nd @ 72°F |
折射率 | 1.49 - | ISO 489 | Nd @ 23°C |