PLEXIGLAS® 8H
PMMA(亚克力)
赢创(原德固赛)(Evonik)
产品描述
PLEXIGLAS® 8H is an amorphous thermoplastic molding compound (PMMA).
Typical properties of PLEXIGLAS® molding compounds are:
good flow
high mechanical strength, surface hardness and mar resistance
high light transmission
very good weather resistance
free colorability due to crystal clarity.
Special properties of PLEXIGLAS® 8H molding compound are:
optimum mechanical properties
increased heat deflection temperature
high melt strength
AMECA listing.
Application:
Used for extruding optical and technical profiles and sheets.
Examples:
sheets, tubes, multi-skin sheets, coextrusion of window profiles and similar applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热良好光学性导光颜色稳定/易着色耐候性高流动高熔体强度 | |||
| 法规认证 | AMECA(美国加拿大汽车认证) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 挤出片材挤出型材挤出管材挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 0.8 cm³/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 78 Mpa | ISO 527 | 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 6.5 % | ISO 527 | 5 mm/min |
拉伸模量 | 3300 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 20 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 108 °C | ISO 306 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 80 E-6/K | ISO 11359 | 0 - 50°C |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | IEC 60695-11-10 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ISO 13468-2 | 3 mm, D65 |
折射率 | 1.49 - | ISO 489 | 3 mm, 589nm/23°C |