Plexiglas® GT3
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Plexiglas® GT3 is tailored for ultimate gloss retention and distinctness of image after thermoforming. It is designed to be used in conjunction with a Solarkote®capstock.
Properties:
Excellent weatherability*
Clear coat system
Enhanced gloss technology
Post forming gloss retention
Excellent scratch resistant
Excellent surface hardness
*does not provide UV screening.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高光泽耐刮擦良好粘合性耐候性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.18 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 1.8 g/10 min | ASTM D 1238 | |
吸水率 | 0.4 % | ASTM D570 | 24 hr immersion |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 61.3 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 18 % | ASTM D638 | |
弯曲强度 | |||
屈服(yld) | 100 Mpa | ASTM D790 | |
弯曲模量 | 2758 Mpa | ASTM D790 | |
拉伸模量 | 3068 Mpa | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 21.4 J/m | ASTM D256 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 80 M | ASTM D 785 | |
铅笔硬度 | |||
- | 5H~7H - | ASTM D 3363 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 94 °C | ASTM D648 | annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 88 °C | ASTM D648 | annealed |
维卡软化温度(Vicat) | 106 °C | ASTM D1525 | 50°C/hr; 10N |
维卡软化温度(Vicat) | 99 °C | ASTM D1525 | 50°C/hr; 50N |
导热系数 | 0.22 W/(m K) | ASTM C 177 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | 3.2 mm |
雾度 | 2 % | ASTM D1003 | 3.2 mm |