PLEXIGLAS® Satinice df23 zk6BR

PLEXIGLAS® Satinice df23 zk6BR

PLEXIGLAS® Satinice df23 zk6BR

PMMA(亚克力)

罗姆化学(原赢创)(Rohm/Roehm Chemical)

产品描述

PLEXIGLAS® Satinice df23 zk6BR, based on PLEXIGLAS® Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light. 


Typical properties of impact modified PLEXIGLAS® molding compound are 

• high break resistance and impact strength 

• improved resistance to stress cracking 

• good weather resistance 

• high surface hardness and mar resistance 

• the pleasant feel and sound of the moldings. 


PLEXIGLAS® df23 zk6BR is characterized by the following special properties: 

 • excellent lightdiffusion combined with excellent light transmittance 

• matte surfaces can be obtained by varying the extrusion parameters. 


Application: 

Used for extruding profiles and sheets, but also for injection molding items for lighting engineering applications

基本信息
原厂资料
物性表(英文)
产品特性
增韧/冲击改性
光扩散
透光
良好表面
耐刮擦
耐候性
添加助剂
光扩散剂
抗冲击剂
颜色形状
粒状
透明
成型方式
注塑
挤出
片材挤出
型材挤出
技术参数
物理性能 值/单位 测试标准 测试条件

密度

1.15 g/cm³ ISO 1183

熔体体积流动速率(MVR)

230℃/3.8 kg

1.3 cm³/10 min ISO 1133
机械性能 值/单位 测试标准 测试条件

拉伸强度

屈服(yld)

46 Mpa ISO 527
50 mm/min

拉伸延伸率

屈服(yld)

5 % ISO 527
50 mm/min

标称断裂伸长率

36 % ISO 527

拉伸模量

1900 Mpa ISO 527
1 mm/min
冲击性能 值/单位 测试标准 测试条件

简支梁缺口(Charpy Notched)

23℃ (73℉)

6 kJ/m² ISO 179/1eA

简支梁无缺口(Charpy Unnotched)

23℃ (73℉)

50 kJ/m² ISO 179/1eU
热学性能 值/单位 测试标准 测试条件

热变形温度(HDT)

0.45 Mpa (66 psi)(4.6kg/cm²)

99 °C ISO 75

1.8 Mpa (264 psi)(18.6kg/cm²)

93 °C ISO 75

维卡软化温度(Vicat)

99 °C ISO 306/B50
B / 50

线性膨胀系数(CLTE)

-

90 E-6/K ISO 11359
0-50 °C

玻璃化温度(Tg)

109 °C ISO 11357
燃烧性能 值/单位 测试标准 测试条件

灼热丝点燃温度(GWIT)

-

700 °C IEC 60695-2-13
光学性能 值/单位 测试标准 测试条件

透光率

81 % ISO 13468-2
3mm, D65

半衰角

21 - DIN 5036
3mm