PLEXIGLAS® Hi-Gloss NTA-3
PMMA(亚克力)
赢创(原德固赛)(Evonik)
产品描述
PLEXIGLAS® Hi-Gloss NTA-3 is a compound with an increased heat deflection temperature based on polymethyl methacrylate (PMMA).
Besides the well-known properties of PLEXIGLAS® molding compound, such as
good flow
high mar resistance
good weather resistance
good polishability,
PLEXIGLAS® Hi-Gloss NTA-3 offers the added benefit of
increased heat deflection temperature under load.
Application:
PLEXIGLAS® Hi-Gloss NTA-3 is particularly suitable for injection molding technical components. Owing to its superior brilliance, high-gloss (Class A) surfaces can be obtained in opaque colors.
Examples:
automotive body parts: window channels, pillar panels
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热高光泽耐刮擦耐候性高流动 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.18 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 2 cm³/10 min | ISO 1133 | |
吸水率 | 3 % | ISO 62 | saturation, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 60 Mpa | ISO 527 | 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.6 % | ISO 527 | 5 mm/min |
拉伸模量 | 2900 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 16 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 106 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 106 °C | ISO 75 | |
维卡软化温度(Vicat) | 116 °C | ISO 306 | B / 50 |
玻璃化温度(Tg) | 126 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
灼热丝点燃温度(GWIT) | |||
- | 675 °C | IEC 60695-2-13 |
原材料现货供应: