CYROLITE® G-20 HIFLO
PMMA(亚克力)
罗姆化学(原赢创)(Rohm/Roehm Chemical)
产品描述
CYROLITE® G-20 HIFLO is a PMMA-based copolymer for injection molding and extrusion of medical applications.
Typical properties of CYROLITE® acrylic-based copolymer compounds are:
• High Light Transmittance with little haze
• 5 times the impact resistance of unmodified acrylics
• Resistant to body fluids and many chemicals
• Excellent bonding to PVC tubing
• Can be thermal bonded, ultrasonic and laser welded
• Good heat resistance
• Resistance to EtO, gamma and E-beam sterilization
The special properties of CYROLITE® G-20 HIFLO are:
• Excellent melt flow rate
Application:
Used for injection molding and extrusion of medical device and diagnostics industries.
基本信息
| 原厂资料 | 物性表(英文)-ISO 物性表(英文)-ASTM | |||
| 产品特性 | 高冲击耐热良好光学性透光良好粘合性易焊接食品接触级医疗级电子束灭菌耐伽马射线环氧乙烷灭菌(EtO)耐化学性良好流动性 | |||
| 法规认证 | FDA(食品药品监督管理局)ISO10993(生物相容性)USP Class VI(美国药典) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.11 g/cm³ | ISO 1183 | |
比重 | 1.11 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 6.2 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/5 kg | 10 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.4~0.7 % | ASTM D 955 | |
吸水率 | 0.3 % | ASTM D570 | |
堆积(视)密度 | 0.65 g/cm³ | ASTM D 1895 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 51 Mpa | ISO 527 | 50 mm/min |
- | 48.3 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
屈服(yld) | 3.6 % | ASTM D638 | |
屈服(yld) | 3.4 % | ISO 527 | 50 mm/min |
断裂(brk) | 9.5 % | ASTM D638 | |
标称断裂伸长率 | 11 % | ISO 527 | |
弯曲强度 | |||
- | 64.8 Mpa | ASTM D790 | |
弯曲模量 | 2100 Mpa | ASTM D790 | |
拉伸模量 | 2600 Mpa | ASTM D638 | |
拉伸模量 | 2300 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 11 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
0℃ (32℉) | 59 J/m | ASTM D256 | 6.35 mm |
23℃ (73℉) | 101 J/m | ASTM D256 | 6.35 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 27 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 83 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 86 °C | ASTM D648 | Annealed, 6.35 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 79 °C | ISO 75 | |
维卡软化温度(Vicat) | 101 °C | ASTM D1525 | 50N, 50°C/h |
维卡软化温度(Vicat) | 95 °C | ISO 306/B50 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 92.5 E-6 mm/mm/℃ | ASTM D 696 | 0 to 100°C |
- | 90 E-6/K | ISO 11359 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | IEC 60695-11-10 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 89 % | ASTM D1003 | 3.20 mm |
透光率 | 86 % | ISO 13468-2 | 3 mm, D65 |
雾度 | 6 % | ASTM D1003 | 3 mm |
雾度 | 6 % | ASTM D1003 | 3.20 mm |
折射率 | 1.62 - | ISO 489 | 3 mm, 589nm/23°C |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
黄色指数(YI) | -0.3 - | Internal | 3.20 mm |
原材料现货供应: