Plexiglas® V052i
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Plexiglas® V052i is a lightly impact modified thermoplastic acrylic resin formulated for injection molding. It is characterized by its chemical and heat resistance as well a good melt flow and excellent mold release properties. It is a tougher resin than Plexiglas® V052 allowing improved fabrication. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Moldflow simulation data is available.
基本信息
| 原厂资料 | 物性表-ASTM(英文) 物性表-ISO(英文) 宣传册 (英文) | |||
| 产品特性 | 高冲击高韧性耐热易脱模抗紫外线耐候性耐化学性高流动 | |||
| 添加助剂 | 抗冲击剂 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.18 g/cm³ | ISO 1183 | |
比重 | 1.18 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 2.9 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 3 g/10 min | ASTM D 1238 | |
230°C/3.8 kg | 3.1 g/10 min | ISO 1133 | |
收缩率 | |||
- | 0.2~0.6 % | ASTM D 955 | |
- | 0.2~0.6 % | ISO 294 | |
吸水率 | 0.4 % | ASTM D570 | 24 hr immersion |
吸水率 | 0.4 % | ISO 62 | Method 1, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 70 Mpa | ISO 527-2/1A/5 | |
断裂(brk) | 63.4 Mpa | ASTM D638 | |
断裂(brk) | 60 Mpa | ISO 527-2/1A/5 | |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527-2/1A/5 | |
断裂(brk) | 22 % | ASTM D638 | |
断裂(brk) | 20 % | ISO 527-2/1A/5 | |
弯曲强度 | |||
断裂(brk) | 96.5 Mpa | ASTM D790 | |
- | 85 Mpa | ISO 178/A | Conventional Deflection |
弯曲模量 | 2900 Mpa | ASTM D790 | |
弯曲模量 | 2700 Mpa | ISO 178/A | |
拉伸模量 | 2830 Mpa | ASTM D638 | |
拉伸模量 | 3000 Mpa | ISO 527-2/1A/1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 2 kJ/m² | ISO 179-1/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
- | 20 kJ/m² | ISO 179-1/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 21 J/m | ASTM D256 | |
- | 3 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 84 M | ISO 2039-2 | |
洛氏硬度 M | 84 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 103 °C | ASTM D648 | annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 95 °C | ISO 75-2/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 97.2 °C | ASTM D648 | annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 91 °C | ISO 75-2/A | |
维卡软化温度(Vicat) | 110 °C | ASTM D1525 | 50°C/hr; 10N |
维卡软化温度(Vicat) | 102 °C | ASTM D1525 | 50°C/hr; 50N |
维卡软化温度(Vicat) | 100 °C | ISO 306/B50 | 50N |
维卡软化温度(Vicat) | 108 °C | ISO 306/A50 | 10N |
导热系数 | 0.19 W/(m K) | ASTM C 177 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ASTM D1003 | 0.125 in/3.2 mm |
透光率 | 92 % | ASTM D1003 | 3.2 mm |
雾度 | 1 % | ASTM D1003 | 0.125 in/3.2 mm |
雾度 | 1 % | ASTM D1003 | 3.2 mm |
折射率 | 1.49 - | ASTM D542 | Nd @ 72°F |
折射率 | 1.49 - | ISO 489 | Nd @ 23°C |