ACRYLITE® Hi-Gloss NTA-5 black is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).

Properties
ACRYLITE® molding compounds have the following typical properties:

  • high weather resistance

  • brilliant appearance

  • 100% recyclable


ACRYLITE® Hi-Gloss NTA-5 black is characterized by the following additional properties:

  • highest breaking strength and impact strength

  • increased heat resistance

  • improved resistance to stress cracking

  • balanced property profile


Application areas are:
Add-on automotive body parts, pillar-trims, mirror housings, trim parts at front - and rear end, etc.

基本信息
原厂资料
物性表(英文)
产品特性
高冲击
耐热
高光泽
耐候性
ESCR
颜色形状
粒状
黑色
成型方式
注塑
技术参数
物理性能 值/单位 测试标准 测试条件

密度

1.16 g/cm³ ISO 1183

熔体体积流动速率(MVR)

230℃/3.8 kg

1.3 cm³/10 min ISO 1133

260℃/3.8 kg

8 cm³/10 min ISO 1133

吸水率

1.5 % ISO 62
in water

吸湿率

0.5 % ISO 62
23°C / 50 %
机械性能 值/单位 测试标准 测试条件

拉伸强度

屈服(yld)

54 Mpa ISO 527
50 mm/min

拉伸延伸率

屈服(yld)

5 % ISO 527
50 mm/min

标称断裂伸长率

48 % ISO 527

拉伸模量

2100 Mpa ISO 527
1 mm/min
冲击性能 值/单位 测试标准 测试条件

简支梁无缺口(Charpy Unnotched)

23℃ (73℉)

110 kJ/m² ISO 179/1eU
热学性能 值/单位 测试标准 测试条件

热变形温度(HDT)

0.45 Mpa (66 psi)(4.6kg/cm²)

102 °C ISO 75

1.8 Mpa (264 psi)(18.6kg/cm²)

96 °C ISO 75

维卡软化温度(Vicat)

103 °C ISO 306
B / 50

线性膨胀系数(CLTE)

-

110 E-6/K ISO 11359
0-50 °C

玻璃化温度(Tg)

113 °C ISO 11357
燃烧性能 值/单位 测试标准 测试条件

UL 防火等级

HB

1.6 mm IEC 60707