PLEXIGLAS® Satinice df33 7H

PLEXIGLAS® Satinice df33 7H

PLEXIGLAS® Satinice df33 7H

PMMA(亚克力)

赢创(原德固赛)(Evonik)

产品描述

PLEXIGLAS® Satinice df33 7H, based on PLEXIGLAS® 7H, is characterized by diffuse scattering of light.

Typical properties of impact modified PLEXIGLAS® molding compound are

  • good flow

  • high mechanical strength, surface hardness and mar resistance

  • very good weather resistance.


Extruded parts from PLEXIGLAS® Satinice df33 7H are characterized by the following special properties:

  • excellent light diffusion combined with excellent light transmission

  • semi-gloss surfaces

  • touch and fingerprint resistant.


Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry.

Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.

基本信息
原厂资料
物性表(英文)
产品特性
高冲击
光扩散
导光
低光泽
耐候性
添加助剂
抗冲击剂
颜色形状
粒状
成型方式
挤出
片材挤出
型材挤出
共挤
技术参数
物理性能 值/单位 测试标准 测试条件

密度

1.18 g/cm³ ISO 1183

熔体体积流动速率(MVR)

230℃/3.8 kg

0.9 cm³/10 min ISO 1133
机械性能 值/单位 测试标准 测试条件

拉伸强度

断裂(brk)

65 Mpa ISO 527
5 mm/min

拉伸延伸率

断裂(brk)

4 % ISO 527
5 mm/min

拉伸模量

3300 Mpa ISO 527
1 mm/min
冲击性能 值/单位 测试标准 测试条件

简支梁无缺口(Charpy Unnotched)

23℃ (73℉)

17 kJ/m² ISO 179/1eU
热学性能 值/单位 测试标准 测试条件

热变形温度(HDT)

0.45 Mpa (66 psi)(4.6kg/cm²)

101 °C ISO 75

1.8 Mpa (264 psi)(18.6kg/cm²)

99 °C ISO 75

维卡软化温度(Vicat)

102 °C ISO 306
B / 50

线性膨胀系数(CLTE)

-

66 E-6/K ISO 11359
0 - 50°C
燃烧性能 值/单位 测试标准 测试条件

灼热丝点燃温度(GWIT)

-

700 °C IEC 60695-2-13
光学性能 值/单位 测试标准 测试条件

透光率

69 % ISO 13468-2
3 mm, D65

光泽度

16 - ISO 2813
105 °C

光泽度

9 - ISO 2813
90 °C