Altuglas® HFI 7
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Altuglas® HFI (High Flow and Impact) range offers superior flow and mould release properties for an excellent processability and reduced cycle times, even for the most critical injection works.
HFI materials offer outstanding impact resistance and flexibility but somewhat lower heat and scratch resistance than the MI range.
Altuglas® HFI 7 High impact resistance with very high flow and excellent processability.
基本信息
| 原厂资料 | 物性表(英文) 宣传册 (英文) | |||
| 产品特性 | 高冲击易成型易脱模高流动 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.17 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 11 g/10 min | ISO 1133 | |
收缩率 | |||
- | 0.2~0.6 % | ASTM D 955 | |
吸水率 | 0.33 % | ISO 62 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 48 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
断裂(brk) | 25 % | ISO 527-2 | |
弯曲模量 | 2300 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 3 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
- | 35 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
- | 3.2 kJ/m² | ISO 180/1A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 65 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 83 °C | ISO 75-2 | |
维卡软化温度(Vicat) | 90 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
- | 80 E-6/K | ASTM D 696 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | |
雾度 | 1.5 % | ASTM D1003 | |
折射率 | 1.49 - | ASTM D542 | Method B |