PLEXIGLAS® Satinice df22 zk30
PMMA(亚克力)
罗姆化学(原赢创)(Rohm/Roehm Chemical)
产品描述
PLEXIGLAS® Satinice df22 zk 30 is an amorphous, impact-modified thermoplastic molding compound.
Typical properties of impact modified PLEXIGLAS® molding compounds are:
• high weather resistance
• excellent transmission and clarity
• brilliant appearance
• the pleasant feel and sound of the moldings.
PLEXIGLAS® Satinice df22 zk30 is characterized by the following special properties:
• good light diffusion combined with excellent light transmission
• matte surfaces can be obtained by varying the extrusion parameters
• good break resistance and impact strength
• improved resistance to stress cracking
• balanced property profile
Application:
PLEXIGLAS® Satinice df22 zk 30 is used for injection molding as well as for extruding and coextruding panels and profiles.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性光扩散透光良好表面耐候性 | |||
| 添加助剂 | 光扩散剂抗冲击剂 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出共挤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.16 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 1.1 cm³/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 54 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 4.3 % | ISO 527 | 50 mm/min |
标称断裂伸长率 | 23 % | ISO 527 | |
拉伸模量 | 2200 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 3.1 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 33 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 103 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 101 °C | ISO 75 | |
维卡软化温度(Vicat) | 102 °C | ISO 306/B50 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 96 E-6/K | ISO 11359 | 0-50 °C |
玻璃化温度(Tg) | 112 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | IEC 60695-11-10 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 86 % | ISO 13468-2 | 3mm, D65 |
半衰角 | 11 - | DIN 5036 | 3mm |