Altuglas® HCR 3
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Non impact-modified resin mainly intended for injection moulding, offering:
> Improved chemical resistance specially against alcohols with 3 times higher stress cracking performance than standard V grades.
> Very high heat resistance with 113°C in Vicat B50, allowing shorter cycle times.
> Premium surface hardness and scratch resistance.
Being a pure acrylic resin, Altuglas® HCR 3 offers typical outstanding PMMA optics, UV resistance and mechanical strength.
基本信息
| 原厂资料 | 物性表(英文) 宣传册 (英文) | |||
| 产品特性 | 耐热良好光学性耐刮擦抗紫外线耐化学性耐酒精 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 0.6 g/10 min | ISO 1133 | |
收缩率 | |||
- | 0.2~0.6 % | ASTM D 955 | |
吸水率 | 0.3 % | ISO 62 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 75 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
断裂(brk) | 6 % | ISO 527-2 | |
弯曲模量 | 3300 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 2 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
- | 13 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
- | 1.8 kJ/m² | ISO 180/1A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 99 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 98 °C | ISO 75-2 | |
维卡软化温度(Vicat) | 113 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
- | 65 E-6/K | ASTM D 696 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | |
雾度 | 0.8 % | ASTM D1003 | |
折射率 | 1.49 - | ASTM D542 | Method B |