Arlon® 3000XT
PEEK(聚醚醚酮)
Greene Tweed
产品描述
Primary Industry
-Aerospace
-Energy Upstream
-Semiconductor
Description/Primary Uses
• Virgin PEEK, incorporating Green Tweed’s cross-linking technology
• Back-up rings for HPHT environments
• Harsh oil and gas applications
• V-rings
• Seal-Connect®
• High-temperature insulators
• Engines (Zones 1-3)
• Braking systems
• General seal assemblies
Features & Benefits
• Enhanced mechanical property retention at high temperatures improves performance over current PEEK- and PEKEKK-based solutions
• Increased reliability of critical components over 350°F (177°C)
• Compatible with common aero fluid chemistries; chemical resistance comparable to PEEK
• Superior creep resistance due to cross-linking
• Certified to ISO 23936/NORSOK M-710 for high sour fluid aging
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热阻燃抗蠕变耐化学性耐水解 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.29 g/cm³ | ASTM D792 | |
吸水率 | 0.09 % | ASTM D570 | 24 Hours |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 33.23 Mpa | ASTM D638 | 200°C |
屈服(yld) | 117.9 Mpa | ASTM D638 | 23°C |
屈服(yld) | 28.27 Mpa | ASTM D638 | 260°C |
断裂(brk) | 52.54 Mpa | ASTM D638 | 200°C |
断裂(brk) | 116.5 Mpa | ASTM D638 | 23°C |
断裂(brk) | 37.09 Mpa | ASTM D638 | 260°C |
拉伸延伸率 | |||
断裂(brk) | 25 % | ASTM D638 | 200°C |
断裂(brk) | 8~15 % | ASTM D638 | 23°C |
断裂(brk) | 25 % | ASTM D638 | 260°C |
弯曲强度 | |||
5%应变时 | 40.54 Mpa | ASTM D 790 | 200°C |
5%应变时 | 160.65 Mpa | ASTM D 790 | 23°C |
5%应变时 | 25.79 Mpa | ASTM D 790 | 260°C |
弯曲模量 | 1089.37 Mpa | ASTM D790 | 200°C |
弯曲模量 | 4329.91 Mpa | ASTM D790 | 23°C |
弯曲模量 | 621.91 Mpa | ASTM D790 | 260°C |
拉伸模量 | 1207.69 Mpa | ASTM D638 | 200°C |
拉伸模量 | 3854.17 Mpa | ASTM D638 | 23°C |
拉伸模量 | 607.43 Mpa | ASTM D638 | 260°C |
摩擦系数 | 0.6 - | ASTM D 3702 | Dynamic, PV=5000 psi-ft/min. |
磨损因数 | 110.6 E-10 in3·min/ft·lb·hr | ASTM D 3702 | PV=5000 psi-ft/min. |
剪切强度 | 62.4 Mpa | ASTM D 732 | 200°C |
剪切强度 | 105.49 Mpa | ASTM D 732 | 23°C |
剪切强度 | 47.44 Mpa | ASTM D 732 | 260°C |
压缩模量 | 1558.22 Mpa | ASTM D 695 | 200°C |
压缩模量 | 3619.75 Mpa | ASTM D 695 | 23°C |
压缩模量 | 910.11 Mpa | ASTM D 695 | 260°C |
抗压强度 | 71.02 Mpa | ASTM D 695 | 200°C |
抗压强度 | 151.68 Mpa | ASTM D 695 | 23°C |
抗压强度 | 37.92 Mpa | ASTM D 695 | 260°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
- | 87.6 J/m | ASTM D 256 | |
悬臂梁无缺口(Izod Unnotched) | |||
- | 2018.5 J/m | ASTM D 4812 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 88 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 300 °C | ASTM D648 | Above |
线性膨胀系数(CLTE) | |||
- | 44 E-6 m/m/℃ | ASTM D E831 | -50-50°C |
- | 101 E-6 m/m/℃ | ASTM D E831 | 195-295°C |
- | 189 E-6 m/m/℃ | ASTM D E831 | 350-380°C |
- | 51 E-6 m/m/℃ | ASTM D E831 | 55-135°C |
熔融温度(Tm) | 352 °C | ASTM D3418 | DSC |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | 23°C |
表面电阻率 | 1.0E+15 Ohm | ASTM D257 | 23°C |
介电常数(DK) | |||
1MHz | 1.96 - | ASTM D 150 | 40-mil-thick sample |
绝缘强度 | 29 kV/mm | ASTM D149 | 40-mil-thick sample |