APTIV® 1103 Series Films
PEEK(聚醚醚酮)
威格斯(Victrex)
产品描述
APTIV® 1100 series films are the mineral filled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.
APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom.
APTIV 1100 has a unique combination of properties providing high temperature performance, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen-free and ease of processing makes APTIV films a technology enabler for our customers and end users. APTIV 1100 series provides a higher modulus and lower coefficient of linear thermal expansion over the APTIV 1000 series.
Availability
The films are available in thicknesses from 12 microns up to 125 microns.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高耐久性耐热导热阻燃无卤绝缘低线性膨胀易成型无(低)毒耐化学性耐水解低吸湿性填充增强高阻隔性 | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局)RoHS(欧盟电子电气设备中有害物质) | |||
| 颜色形状 | 薄膜 | |||
| 增强填充 | 30% 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.54 g/cm³ | ISO 1183 | 1103-050M |
收缩率 | |||
纵向(Flow) | 0.5 % | Internal | 1103-050M |
横向(Across Flow) | 0.5 % | Internal | 1103-050M |
吸水率 | 0.09 % | ISO 62 | 50% RH,1103-050M |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 18 E-6/°C | ASTM D 696 | 1103-050M |
导热系数 | 1.3 W/(m K) | ASTM E 1461 | In-Plane |
导热系数 | 0.61 W/(m K) | ASTM E 1461 | Through Plane |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | 23ºC, 100V |
介电常数(DK) | |||
10MHz | 3.5 - | ASTM D150 | 23ºC |
耗散因数(DF) | |||
10MHz | 10 E-4 | ASTM D150 | 23ºC |
绝缘强度 | 200 kV/mm | ASTM D149 | 6.35mm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 90 Mpa | ISO 527-3 | 100µm, MD |
断裂(brk) | 90 Mpa | ISO 527-3 | 100µm, TD |
断裂(brk) | 70 Mpa | ISO 527-3 | 25µm, MD |
断裂(brk) | 70 Mpa | ISO 527-3 | 25µm, TD |
断裂(brk) | 90 Mpa | ISO 527-3 | 50µm, MD |
断裂(brk) | 90 Mpa | ISO 527-3 | 50µm, TD |
断裂(brk) | 90 Mpa | ISO 527-3 | MD, 1103-050M |
断裂(brk) | 90 Mpa | ISO 527-3 | TD, 1103-050M |
拉伸延伸率 | |||
断裂(brk) | 5 % | ISO 527-3 | 100µm, MD |
断裂(brk) | 10 % | ISO 527-3 | 100µm, TD |
断裂(brk) | 10 % | ISO 527-3 | 25µm, MD |
断裂(brk) | 10 % | ISO 527-3 | 25µm, TD |
断裂(brk) | 10 % | ISO 527-3 | 50µm, MD |
断裂(brk) | 10 % | ISO 527-3 | 50µm, TD |
断裂(brk) | 10 % | ISO 527-3 | MD, 1103-050M |
断裂(brk) | 10 % | ISO 527-3 | TD,1103-050M |
拉伸模量 | 5000 Mpa | ISO 527-3 | 100µm, MD |
拉伸模量 | 4500 Mpa | ISO 527-3 | 100µm, TD |
拉伸模量 | 5500 Mpa | ISO 527-3 | 25µm, MD |
拉伸模量 | 4500 Mpa | ISO 527-3 | 25µm, TD |
拉伸模量 | 5500 Mpa | ISO 527-3 | 50µm, MD |
拉伸模量 | 4500 Mpa | ISO 527-3 | 50µm, TD |
拉伸模量 | 5500 Mpa | ISO 527-3 | MD, 1103-050M |
拉伸模量 | 4500 Mpa | ISO 527-3 | TD, 1103-050M |
穿透强度 | 4 kJ/m² | Internal | 1103-050M |
裤形撕裂 | 5 kN/m | ISO 6383-1 | MD, 1103-050M |
裤形撕裂 | 6 kN/m | ISO 6383-1 | TD, 1103-050M |