LNP™ THERMOCOMP™ LX08411
PEEK(聚醚醚酮)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added feature of this material is: Opaque.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 填充增强 | |||
| 颜色形状 | 不透明色 | |||
| 增强填充 | 碳纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.45 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.2~0.28 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.75~0.85 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.03 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 270 Mpa | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 270 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 1.8 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 1.8 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
屈服(yld) | 366 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) | 366 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 25000 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 23510 Mpa | ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 70 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 775 J/m | ASTM D4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 341 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 327 °C | ASTM D648 | 3.2 mm, unannealed |