Celapex® 500G
PEEK(聚醚醚酮)
塞拉尼斯(Celanese)
产品描述
Standard flow PEEK, unreinforced
Celapex® 500G is an standard flow unreinforced polyether ether ketone (PEEK) for injection molding and extrusion. It has superior chemically resistant to aggressive environments. The typical applications of this product are extrusion stock shapes, and injection molded parts with higher impact, ductility, creep, and fatigue.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐疲劳高冲击抗蠕变耐化学性耐水解高粘度 | |||
| 成型方式 | 注塑挤出片材挤出薄膜挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.3 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
380°C/5.0 kg | 10 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.3 % | ISO 294-4, 2577 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 100 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
断裂(brk) | 45 % | ISO 527-2/1A | 50mm/min |
弯曲强度 | |||
- | 165 Mpa | ISO 178 | 23°C |
弯曲模量 | 4100 Mpa | ISO 178 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 7 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 7.5 kJ/m² | ISO 180/1A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 180/1U | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 152 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 120 E-6/°C | ISO 11359-2 | Above Tg |
纵向(Flow) | 45 E-6/°C | ISO 11359-2 | Below Tg |
熔融温度(Tm) | 343 °C | ISO 11357-1/-3 | 10°C/min |
玻璃化温度(Tg) | 143 °C | ISO 11357-1/-2 | 10°C/min |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+14 Ohm-m | IEC 60093 | |
介电常数(DK) | |||
50 Hz | 3 - | IEC 60250 | |
1 kHz | 3.1 - | IEC 60250 | |
耗散因数(DF) | |||
1MHz | 40 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
- | 150 - | IEC 60112 | 100 Drop Voltage |
绝缘强度 | 23 kV/mm | IEC 60243-1 |