VICTREX® PEEK 650G
PEEK(聚醚醚酮)
威格斯(Victrex)
产品描述
High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low flow, FDA food contact compliant, colour natural/beige.
Typical Application Areas:
Applications for higher strength and stiffness as well as enhanced ductility.
Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 食品接触级医疗级耐化学性高粘度 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 颜色形状 | 粒状本色米色 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.3 g/cm³ | ISO 1183 | Crystalline |
收缩率 | |||
纵向(Flow) | 0.9 % | ISO 294-4 | Along flow |
横向(Across Flow) | 1.3 % | ISO 294-4 | Across flow |
吸水率 | 0.55 % | ISO 62-1 | Saturation, 100°C, by immersion |
吸水率 | 0.45 % | ISO 62-1 | Saturation, 23°C, by immersion |
粘度 | 475 Pa-s | ISO 11443 | Melt Viscosity, 400°C |
螺旋流 | 125 mm | - | 395°C nozzle, 180°C tool, 1mm thick |
螺旋流 | 630 mm | - | 395°C nozzle, 180°C tool, 3mm thick |
螺旋流 | 700 mm | - | 415°C nozzle, 180°C tool, 3mm thick |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 95 Mpa | ISO 527 | 23°C |
拉伸延伸率 | |||
断裂(brk) | 60 % | ISO 527 | 23°C |
弯曲强度 | |||
屈服(yld) | 155 Mpa | ISO 178 | 23°C |
3.5%应变 | 120 Mpa | ISO 178 | 23°C |
- | 85 Mpa | ISO 178 | 125°C |
- | 16 Mpa | ISO 178 | 175°C |
- | 9 Mpa | ISO 178 | 275°C |
弯曲模量 | 3600 Mpa | ISO 178 | 23°C |
拉伸模量 | 3900 Mpa | ISO 527 | 23°C |
抗压强度 | 65 Mpa | ISO 604 | 120°C |
抗压强度 | 120 Mpa | ISO 604 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/U | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 9.5 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 180/U | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 84 D | ISO 868 | 23°C |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 168 °C | ISO 75/Af | Annealed 200°C / 4h |
1.8 Mpa (264 psi)（18.6kg/cm²） | 152 °C | ISO 75/Af | As moulded |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 125 E-6/K | ISO 11359 | Along flow above 143°C |
纵向(Flow) | 45 E-6/K | ISO 11359 | Along flow below 143°C |
横向(Across Flow) | 160 E-6/K | ISO 11359 | Average above 143°C |
横向(Across Flow) | 65 E-6/K | ISO 11359 | Average below 143°C |
熔融温度(Tm) | 343 °C | ISO 11357 | |
玻璃化温度(Tg) | 150 °C | ISO 11357 | Midpoint |
玻璃化温度(Tg) | 143 °C | ISO 11357 | Onset |
导热系数 | 0.32 W/(m K) | ISO 22007-4 | Along flow, 23°C |
导热系数 | 0.29 W/(m K) | ISO 22007-4 | Average, 23°C |
加工温度 | 375~395 °C | - | |
模具温度 | 170~200 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
灼热丝可燃性指数(GWFI) | |||
2mm | 960 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | 125°C |
体积电阻率 | 1.0E+16 Ohm-cm | IEC 60093 | 23°C |
体积电阻率 | 1.0E+9 Ohm-cm | IEC 60093 | 275°C |
介电常数(DK) | |||
1 kHz | 3.1 - | IEC 60250 | 23°C |
耗散因数(DF) | |||
1MHz | 50 E-4 | IEC 60250 | 23°C |
相比漏电起痕指数(CTI ) | |||
- | 150 V | IEC 60112 | |
绝缘强度 | 23 kV/mm | IEC 60243-1 | 2mm thickness |