VICTREX® PEEK 90HMF40
PEEK(聚醚醚酮)
威格斯(Victrex)
产品描述
High performance thermoplastic material, 40% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, colour black.
Typical Application Areas:
Complex geometries with thinner cross sections or longer flow length where superior strength in a static or dynamic system is required. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐磨低摩擦低线性膨胀耐化学性良好流动性填充增强 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 40% 碳纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.45 g/cm³ | ISO 1183 | Crystalline |
收缩率 | |||
纵向(Flow) | 0 % | ISO 294-4 | Along flow |
横向(Across Flow) | 0.4 % | ISO 294-4 | Across flow |
吸水率 | 0.4 % | ISO 62-1 | Saturation, 100°C, by immersion |
吸水率 | 0.3 % | ISO 62-1 | Saturation, 23°C, by immersion |
粘度 | 300 Pa-s | ISO 11443 | Melt Viscosity, 400°C |
螺旋流 | 100 mm | - | 380°C nozzle, 190°C tool, 1mm thick |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 220 Mpa | ISO 527 | 120°C |
断裂(brk) | 145 Mpa | ISO 527 | 180°C |
断裂(brk) | 330 Mpa | ISO 527 | 23°C |
断裂(brk) | 85 Mpa | ISO 527 | 275°C |
拉伸延伸率 | |||
断裂(brk) | 1.2 % | ISO 527 | 23°C |
弯曲强度 | |||
- | 350 Mpa | ISO 178 | 120°C |
- | 220 Mpa | ISO 178 | 180°C |
- | 475 Mpa | ISO 178 | 23°C |
- | 120 Mpa | ISO 178 | 275°C |
弯曲模量 | 37000 Mpa | ISO 178 | 23°C |
拉伸模量 | 43000 Mpa | ISO 527 | 23°C |
抗压强度 | 250 Mpa | ISO 604 | 120°C |
抗压强度 | 120 Mpa | ISO 604 | 200°C |
抗压强度 | 310 Mpa | ISO 604 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 8 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 60 kJ/m² | ISO 179/U | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 10.5 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 60 kJ/m² | ISO 180/U | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 88.5 D | ISO 868 | 23°C |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 349 °C | ISO 75f | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 1 E-6/K | ISO 11359 | Along flow above 143°C |
纵向(Flow) | 3 E-6/K | ISO 11359 | Along flow below 143°C |
横向(Across Flow) | 80 E-6/K | ISO 11359 | Average above 143°C |
横向(Across Flow) | 35 E-6/K | ISO 11359 | Average below 143°C |
熔融温度(Tm) | 343 °C | ISO 11357 | |
玻璃化温度(Tg) | 143 °C | ISO 11357 | Onset |
导热系数 | 4.3 W/(m K) | ISO 22007-4 | Along flow, 23°C |
导热系数 | 2 W/(m K) | ISO 22007-4 | Average, 23°C |
加工温度 | 365~385 °C | - | |
模具温度 | 190~200 °C | - | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1E+5 Ohm-cm | ASTM D 4496 | 23°C, 1V |