LNP™ THERMOCOMP™ LF006EX1
LNP™ THERMOCOMP™ LF006EX1
PEEK(聚醚醚酮)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP LF006EX1 is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. Added features of this material include: low warpage, easy Molding.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 低翘曲易成型填充增强 |
| 增强填充 | 30% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.532 g/cm³
| ISO 1183 | |
比重 | 1.536 -
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.43 % | ASTM D 955 | 24 hrs |
横向(Across Flow) |
0.65 % | ASTM D 955 | 24 hrs |
吸湿率 | 0.088 %
| ISO 62 | 23°C / 50% RH |
吸湿率 | 0.037 %
| ASTM D 570 | 23°C/50% RH/24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
164 Mpa | ISO 527 | |
断裂(brk) |
171 Mpa | ASTM D638 | |
拉伸延伸率 | | | |
断裂(brk) |
1.98 % | ASTM D638 | |
断裂(brk) |
1.87 % | ISO 527 | |
弯曲强度 | | | |
- |
235 Mpa | ASTM D790 | |
- |
225 Mpa | ISO 178 | |
弯曲模量 | 10100 Mpa
| ASTM D790 | |
弯曲模量 | 10183 Mpa
| ISO 178 | |
拉伸模量 | 12280 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 11820 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | | | |
23℃ (73℉) |
46 kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
95 J/m | ASTM D256 | |
23℃ (73℉) |
10 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
732 J/m | ASTM D4812 | |
23℃ (73℉) |
47.14 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
336 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） |
333 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
321 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
309 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
22.3 E-6/°C | ASTM E831 | -40°C to 120°C, flow |
横向(Across Flow) |
41 E-6/°C | ASTM E831 | -40°C to 120°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | | | |
1.1 GHz |
3.82 - | Internal | |
1.9 GHz |
3.84 - | Internal | |
耗散因数(DF) | | | |
1.1 GHz |
39 E-4 | Internal | |
1.9 GHz |
41 E-4 | Internal | |