VICTREX® PEEK 650CA30
PEEK(聚醚醚酮)
威格斯(Victrex)
产品描述
High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low flow, FDA food contact compliant, colour black.
Typical Application Areas:
Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐磨低摩擦低线性膨胀食品接触级高粘度填充增强 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑挤出 | |||
| 增强填充 | 30% 碳纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.4 g/cm³ | ISO 1183 | Crystalline |
收缩率 | |||
纵向(Flow) | 0.1 % | ISO 294-4 | Along flow |
横向(Across Flow) | 0.5 % | ISO 294-4 | Across flow |
吸水率 | 0.45 % | ISO 62-1 | Saturation, 100°C, by immersion |
吸水率 | 0.3 % | ISO 62-1 | Saturation, 23°C, by immersion |
粘度 | 800 Pa-s | ISO 11443 | Melt Viscosity, 420°C |
螺旋流 | 80 mm | - | 415°C nozzle, 200°C tool, 1mm thick |
螺旋流 | 375 mm | - | 415°C nozzle, 200°C tool, 3mm thick |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 150 Mpa | ISO 527 | 125°C |
断裂(brk) | 85 Mpa | ISO 527 | 175°C |
断裂(brk) | 250 Mpa | ISO 527 | 23°C |
断裂(brk) | 50 Mpa | ISO 527 | 275°C |
拉伸延伸率 | |||
断裂(brk) | 1.9 % | ISO 527 | 23°C |
弯曲强度 | |||
- | 250 Mpa | ISO 178 | 125°C |
- | 120 Mpa | ISO 178 | 175°C |
- | 370 Mpa | ISO 178 | 23°C |
- | 60 Mpa | ISO 178 | 275°C |
弯曲模量 | 21500 Mpa | ISO 178 | 23°C |
拉伸模量 | 25000 Mpa | ISO 527 | 23°C |
抗压强度 | 180 Mpa | ISO 604 | 120°C |
抗压强度 | 60 Mpa | ISO 604 | 200°C |
抗压强度 | 280 Mpa | ISO 604 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 10.5 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 60 kJ/m² | ISO 179/U | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 12 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 60 kJ/m² | ISO 180/U | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 333 °C | ISO 75f | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 6 E-6/K | ISO 11359 | Along flow above 143°C |
纵向(Flow) | 6 E-6/K | ISO 11359 | Along flow below 143°C |
横向(Across Flow) | 135 E-6/K | ISO 11359 | Average above 143°C |
横向(Across Flow) | 50 E-6/K | ISO 11359 | Average below 143°C |
熔融温度(Tm) | 343 °C | ISO 11357 | |
玻璃化温度(Tg) | 150 °C | ISO 11357 | Midpoint |
玻璃化温度(Tg) | 143 °C | ISO 11357 | Onset |
导热系数 | 2 W/(m K) | ISO 22007-4 | Along flow, 23°C |
导热系数 | 0.95 W/(m K) | ISO 22007-4 | Average, 23°C |
加工温度 | 390~415 °C | - | |
模具温度 | 180~210 °C | - | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1E+5 Ohm-cm | ASTM D 4496 | 23°C, 1V |