LNP™ THERMOCOMP™ LC00APXQ
LNP™ THERMOCOMP™ LC00APXQ
PEEK(聚醚醚酮)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP LC00APXQ is a compound based on Polyetheretherketone resin containing 50% Carbon Fiber. Added features of this material include: Exceptional Processing, Electrically Conductive.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 导电易成型填充增强 |
| 增强填充 | 50% 碳纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
比重 | 1.48 -
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.13~0.25 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
0.6~1.3 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.03 %
| ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
320 Mpa | ISO 527 | 5 mm/min |
断裂(brk) |
328 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
1.2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) |
1.1 % | ISO 527 | 5 mm/min |
弯曲强度 | | | |
断裂(brk) |
505 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- |
473 Mpa | ISO 178 | |
弯曲模量 | 40500 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 40730 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 49800 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 47400 Mpa
| ISO 527 | 1 mm/min |
泊松比 | 0.45 -
| ASTM E 132 | |
剪切强度 | 114 Mpa
| ASTM D 732 | |
剪切模量 | 5187 Mpa
| ASTM D 732 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
77 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
768 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
7 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
335 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
2 E-6/°C | ASTM E831 | -40°C to 150°C, flow |
横向(Across Flow) |
20 E-6/°C | ASTM E831 | -40°C to 150°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+2~1E+3 Ohm
| ASTM D257 | |