LNP™ LUBRICOMP™ LL004C
PEEK(聚醚醚酮)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP LL004C is a compound based on Polyetheretherketone resin containing 20% PTFE. Added features of this material include: Wear Resistant,Clean Compounding System.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨 | |||
| 增强填充 | 20% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.37 g/cm³ | ISO 1183 | |
密度 | 1.37 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 1.3 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 1.3 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1.9 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 1.85 % | ISO 294 | xflow, 24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 74 Mpa | ASTM D638 | |
屈服(yld) | 73 Mpa | ISO 527 | |
断裂(brk) | 69 Mpa | ISO 527 | |
断裂(brk) | 69 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 5.8 % | ASTM D638 | |
屈服(yld) | 5 % | ISO 527 | |
断裂(brk) | 23.3 % | ASTM D638 | |
断裂(brk) | 11.8 % | ISO 527 | |
弯曲强度 | |||
- | 117 Mpa | ASTM D790 | |
- | 118 Mpa | ISO 178 | |
弯曲模量 | 2960 Mpa | ASTM D790 | |
弯曲模量 | 3320 Mpa | ISO 178 | |
拉伸模量 | 2890 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 3060 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.52 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.43 - | ASTM D 3702 | Static COF |
磨损因数 | 1.28 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 96 J/m | ASTM D256 | |
23℃ (73℉) | 8 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1548 J/m | ASTM D4812 | |
23℃ (73℉) | 91 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 3 J | ASTM D3763 | |
多轴冲击 | 1 J | ISO 6603 |