LNP™ THERMOCOMP™ LC008EXQ
LNP™ THERMOCOMP™ LC008EXQ
PEEK(聚醚醚酮)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP LC008EXQ is a compound based on Polyetheretherketone containing 40% Carbon Fiber. Added features of this grade include: Electrically Conductive, Easy Molding.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 导电易脱模填充增强 |
| 增强填充 | 40% 碳纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
比重 | 1.44 -
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.15~0.3 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
0.7~1.4 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.05 %
| ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
321 Mpa | ISO 527 | 5 mm/min |
断裂(brk) |
330 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
1.5 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) |
1.4 % | ISO 527 | 5 mm/min |
弯曲强度 | | | |
屈服(yld) |
492 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- |
460 Mpa | ISO 178 | |
弯曲模量 | 35200 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 33820 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 41480 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 40420 Mpa
| ISO 527 | 5 mm/min |
泊松比 | 0.47 -
| ASTM E 132 | |
剪切强度 | 126 Mpa
| ASTM D 732 | |
剪切模量 | 5003 Mpa
| ASTM D 732 | |
抗压强度 | 215 Mpa
| Internal | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
82 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
863 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
7 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
335 °C | ASTM D648 | 3.2 mm, unannealed |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+2~1E+3 Ohm
| ASTM D257 | |