KetaSpire® KT-820 SL45
PEEK(聚醚醚酮)
索尔维(苏威)(Solvay)
产品描述
KetaSpire® KT-820 SL45 is a PEEK based compound specifically designed to provide exceptionally low wear rates and good mechanical properties in applications where an external lubricant is provided.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 耐疲劳耐热阻燃耐磨低摩擦尺寸稳定耐化学性填充增强 | |||
法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
颜色形状 | 粒状黑色 | |||
成型方式 | 注塑型材挤出机加工 | |||
增强填充 | 碳纤PTFE碳纤+PTFE |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
比重 | 1.5 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
400℃/2.16 kg | 2 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0~0.2 % | ASTM D 955 | 3.18 mm |
横向(Across Flow) | 1.3~1.5 % | ASTM D 955 | 3.18 mm |
吸水率 | 0.03 % | ASTM D570 | 24 hr |
粘度 | 380 Pa-s | ASTM D 3835 | 400℃,1000 sec-1 |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 197 Mpa | ISO 527-2/1A/5 | |
- | 161 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
断裂(brk) | 1.5 % | ASTM D638 | 5.0 mm/min |
断裂(brk) | 1.5 % | ISO 527-2/1A/5 | |
弯曲强度 | |||
- | 265 Mpa | ASTM D790 | |
- | 273 Mpa | ISO 178 | |
弯曲模量 | 16600 Mpa | ASTM D790 | |
弯曲模量 | 24100 Mpa | ISO 178 | |
拉伸模量 | 18300 Mpa | ASTM D638 | |
拉伸模量 | 25300 Mpa | ISO 527-2/1A/1 | |
摩擦系数 | 0.45 - | ASTM D 3702 | Dry conditions: 200 fpm and 125 psi |
摩擦系数 | 0.34 - | ASTM D 3702 | Dry conditions: 800 fpm and 31.25 psi |
摩擦系数 | 0.12 - | ASTM D 3702 | Lubricated conditions: 75 fpm and 1000 psi |
摩擦系数 | 0.07 - | ASTM D 3702 | Lubricated conditions: 800 fpm and 750 psi |
剪切强度 | 84.1 Mpa | ASTM D 732 | |
抗压强度 | 127 Mpa | ASTM D 695 | |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
- | 69 J/m | ASTM D 256 | |
- | 8.5 kJ/m² | ISO 180 | |
悬臂梁无缺口(Izod Unnotched) | |||
- | 43 kJ/m² | ISO 180 | |
- | 530 J/m | ASTM D 4812 | |
硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 90 M | ASTM D 785 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)(18.6kg/cm²) | 299 °C | ASTM D648 | Annealed |
比热容 | 1670 J/kg/℃ | DSC | 200℃ |
比热容 | 1250 J/kg/℃ | DSC | 50℃ |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 17 E-6 cm/cm/℃ | ASTM E831 | -50 to 50℃ |
熔融温度(Tm) | 342 °C | ASTM D3418 | |
玻璃化温度(Tg) | 152 °C | ASTM D 3418 | |
导热系数 | 0.36 W/(m K) | ASTM E 1530 |