LNP™ THERMOCOMP™ LC006EXQ
LNP™ THERMOCOMP™ LC006EXQ
PEEK(聚醚醚酮)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP LC006EXQ is a compound based on Polyetheretherketone containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 导电易脱模填充增强 |
| 增强填充 | 30% 碳纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
比重 | 1.4 -
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.15~0.3 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
0.7~1.4 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.05 %
| ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
319 Mpa | ISO 527 | 5 mm/min |
断裂(brk) |
314 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
1.7 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) |
1.5 % | ISO 527 | 5 mm/min |
弯曲强度 | | | |
断裂(brk) |
477 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- |
457 Mpa | ISO 178 | |
弯曲模量 | 27100 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 27230 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 31700 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 35320 Mpa
| ISO 527 | 1 mm/min |
泊松比 | 0.44 -
| ASTM E 132 | |
剪切强度 | 119 Mpa
| ASTM D 732 | |
剪切模量 | 4756 Mpa
| ASTM D 732 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
75 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
936 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
6 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
332 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
5 E-6/°C | ASTM E831 | -40°C to 150°C, flow |
横向(Across Flow) |
30 E-6/°C | ASTM E831 | -40°C to 150°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+3~1E+4 Ohm
| ASTM D257 | |